Silicone structured stucco «Lamb» size of grain 1,5 mm Farbex

Silicone structured stucco «Lamb» Farbex


Silicone structured stucco «Lamb»

size of grain 1,5 mm


The product is ready to use. It creates a weather-resistant coating with low water permeability, resistance to mechanic load, aggressive effect of nature and different dirt. It is vapor permeable, flexible, has high adhesion. It can cover small cracks. It is easy to use and to form a structure.

Sphere of application

The plaster is used as a finishing coating with a structure "lamb" when the coating of porous and gas concrete surfaces, mineral stuccos. gypsum panels, concrete, gypsum surfaces, insulating systems, walls made of stone, asbestos cement indoors and outdoors. It is recommended for coating of the surfaces with high exploiting load and for insulation of facades.


It can be tinted manually with Pigment Concentrate Farbex Color, other waterborne coloring pastes or with a coloring machine acc. to NCS color range and others.

Technical data

Consumption standard of 1 layer 2,5-2,9 kg/m2
Thinner Water
Application Apply the product with a stainless trowel and form a sturcture with a plactic surfaces.
Drying period (23 °С, 50% RH) ab. 2 hours ("to touch"). After application the surface shall not be effected by falls or frost during 24 hours. Complete drying of the surface is in 72 hours.
Solids content (DSTU ISO 3251) ab. 80 %
Density (DSTU ISO 2811-1) ab. 1,9 г/см3
Gloss (DSTU ISO 2813) Not defined
Dry film thickness It corresponds the size of the grain, ab. 1,5 mm
Particle size maximal 1500 microns
Vapor permeability (EN ISO 7783-2) more than 150 g/(m2*24hours)
Water permeability (DSTU EN 1062-3) max. 0,1 kg/(m2*h0,5)
Marking acc. to the DSTU EN 1062-1 G0|E5|S3|V1|W3|A0|C0
Warranty period 24 months
Packaging 18 kg, 30 kg


white (base A)

Application instruction

1. Preliminary preparation

Uncoated surfaces: Clean thoroughly from loose coatings, dust, oil, grease and other dirt.  New stucco coatings shall not be treated before 2-4 weeks.

Coated surfaces: Clean the surface thoroughly from old loose coatings (loose paint or varnish) in mechanical (a scraper, a wire brush), thermal (hot air fan, infrared radiation) or chemical way (paint removal solution). Chalk and lime-chalk coatings shall be removed till hard surface mechanically. The surface shall be cleaned from different dirt. Surfaces previously coated with alkyd or oily enamels shall be sandpapered and then apply Beton-kontakt TM Farbex. Then treat the surface as uncoated surfaces.

Defects of the surfaces shall be plastered.

It is recommended to treat the surface with Antiseptic TM Farbex for protection against mould and fungi.

2. Priming

Extremely absorbing surfaces shall be treated with Deep penetrating silicone primer TM Farbex.

It is necessary to apply a layer of  Silicone Primer Paint with quartz filler TM Farbex. Primer paint shall be tinted in the color of decorative stucco.

Beton kontakt TM Farbex shall be applied in one layer in the case of complicated bases. Also, it shall be tinted in the color of decorative stucco.


3. Applying

Stir carefully before use.

The product shall be applied on the surface in 1 layer with a stainless trowel or suitable machine for application. Remove extra product from the surface right after application making grain-size thickness of the layer and evenly structured with plastic plasterer's trowel. Depending on the direction of the tool move (vertical, horizontal, or circle-like, etc.) different structures of the "bark beetle" are achieved.  

If appliction is performed manually there shall be two persons as the work on one flat area shall be performed constantly with the "wet to wet" method. The structure of the surface shall be formed with the same instrument on the whole surface. Don't let the edge of applied product getting dry.

When the product is applied with machine the nozzle shall be chosen exactly in accordance with the size of the grain (nozzle size shall have a diameter of 4 grains). Necessary working pressure shall be 0.3 - 0.4 MPa (3-4 bar). If the required structure achieved with machine application, there is no need to use structure-forming tools.

The temperature of air and the surface under application shall be from +5 ° С till +30 ° С, maximal relative air humidity shall be 80%.

Do not apply the stucco under direct sunlight, strong wind, frost and atmospheric precipitation.

4. Tool cleaning

Clean tools with water after application. Do not let them dry. Dry product shall be removed  from the tools in mechanical way.

Силіконові штукатурки Farbex
На ринку лакофарбової продукції є безліч матеріалів для фінішної обробки фасаду будівлі. Частіше всього вибір лягає на декоративні штукатурки. При утепленні будинку мінеральною ватою, в якості фінішного покриття використовується силіконова фасадна штукатурка Баранець та Короїд. Основні переваги штукатурки на силіконовій основі:
  • висока паропроникність;
  • стійкість до миття;
  • самоочищення під дією опадів;
  • гарна пластичність;
  • низька водопроникність.
У нас в асортименті є готова до використання силіконова штукатурка.  Вам не доведеться витрачати час та зусилля на приготування суміші. Силіконова штукатурка простий та легкий в нанесенні матеріал, який не боїться механічних навантажень, агресивних впливів навколишнього середовища. Штукатурка на силіконовій основі здатна перекривати дрібні тріщини. Силіконова штукатурка має декілька різновидів декоративного покриття:
  • Баранець;
  • Короїд.
Силіконову штукатурку Баранець тао Короїд можна придбати за доступною ціною:
  • в інтернет-магазині Farbex з доставкою по всій Україні;
  • у популярних будівельних мережах: Епіцентр, Леруа Мерлен, Нова Лінія та 33м2.
Майстрам та будівельним компаніям ціну на силіконовий Баранець та Короїд, а також інформацію про подальшу співпрацю можна дізнатися, звернувшись до відділу прямих продажів: (050) 425 84 00 та (067) 544 03 02.



Flow calculator

Consumption standard of 1 layer

When calculating the area to be painted, you need to subtract the area that will not be painted. (windows, doors, etc.)

Paint consumption may vary depending on dilution and uniformity of application of the paint.