Silicone facade paint Farbex

Silicone facade paint Farbex


Silicone facade paint


Matt. It has advanced resistance to weather effects (moisture, UV radiation). It has high vapor and low water permeability (acc. to DSTU EN 1062), and good adhesion.

Sphere of application

It is intended for coating of building facades made of different hard mineral (concrete, bricks, plaster, putty, gypsum base surface), mineralpolimeric (acrylic or silicone stuccos) and other surfaces (ply wood, MDF, wood chip board, OSB).

It is used for the initial application and renovation of facades of living, trade, industrial, storing and other buildings, reinforced concrete and cast-in-place concrete constructions and also facade insulation systems.


It can be tinted manually with Pigment Concentrate Farbex Color, other waterborne coloring pastes or with a coloring machine acc. to NCS color range and others.

Technical data

Consumption standard of 1 layer 150-200 g/m2
Thinner Water
Application Apply with a roller, a brush or a spraying gun.
Drying period (23 °С, 50% RH) 2 hours
Color base А, B, TR. It is shaded according to NCS color range.
Solids content (DSTU ISO 3251) about 56 % (base А),
about 55 % (base B),
about 56 % (base TR).
Density (DSTU ISO 2811-1) about 1,45 g/сm3 (base А),
about 1,37 g/cm3 (base B),
about 1,36 g/cm3 (base TR).
Gloss (DSTU ISO 2813) < 5 GU
Dry film thickness 50-100 microns
Particle size max. 30 microns
Vapor permeability (EN ISO 7783-2) more than 150 g/(m2*day)
Water permeability (DSTU EN 1062-3) max. 0,1 kg/(m2* h0,5)
Marking acc. to the DSTU EN 1062-1 G3|E2|S1|V1|W3|A0|C0
Warranty period 24 months from the matufacturing date
(at the temperature from +5 °С till +35 °С)
Packaging Base А - 1,4 kg, 4,2 kg, 7 kg, 14 kg, 20 kg
Base B, TR - 1,2 kg, 3,6 kg, 6 kg, 12 kg, 18 kg




base B
base TR
white (base A)

Application instruction

1. Preliminary preparation

Uncoated surfaces: clean of fragile surfaces till hard base surface. Remove dust, oil, grease and other dirt. 

Previously coated surfaces: clean thoroughly the surface of old loose coats (pealed paint or varnish) in mechanical (a scraper or a wire brush), thermal (hot air dryer, infrared radiation) or chemical (paint removing solutions) way. Chalk or lime-chalk coatings shall be removed till hard surface in mechanical way. The surfaces shall be also cleaned from all kinds of dirt. Surfaces, previously coated with alkyd or oil enamels, shall be sandpapered. Then treat the surface as the uncoated one.

Non-significant defects of the mineral surface shall be corrected with Putty TM Farbex. Then sandpaper it.

It is recommended to treat the surface with antiseptic Farbex for protection against mould and fungi.

2. Priming

Previously treated mineral and wooden surfaces need no undercoating.

Previously untreated absorbing mineral surfaces shall be undercoated with Silicone deep-penetrating primer TM Farbex.

Previously uncoated wooden surfaces shall be undercoated with wood protective acrylic primer TM Maxima.

3. Application

Stir the paint thoroughly before use. Dilute with water if necessary. Abnormal dilution makes the quality of the coat worse! Apply the paint at the temperature of air and surface from + 5 °С till + 35 °С and relative air humidity less than 80%. Apply the paint with 1-2 coats with a brush, a roller or a spraying gun.

Do not apply the paint under direct sunlight, strong wind, frost or precipitation. The coating shall not be affected with precipitation or sub-zero temperatures for 8 hours after it is applied.

The surface achieves its protective properties in 24 hours.

4. Tool cleaning

Clean tools with water after application. Do not let them dry. The dry product shall be removed from the tools in a mechanical way.


Flow calculator

Consumption standard of 1 layer

When calculating the area to be painted, you need to subtract the area that will not be painted. (windows, doors, etc.)

Paint consumption may vary depending on dilution and uniformity of application of the paint.